TESTING DATA |
||
|
PROPERTY |
STANDARD |
RESULT |
|
Strength |
||
|
Cold Temperature Pliability |
ASTM C765 Standard Test Method for Low-Temperature Flexibility of Preformed Tape |
MD: PASS (no cracking) |
|
Ultimate Tensile Strength |
ASTM D882 Standard Test Method for Tensile Properties of Thin Plastic Sheeting |
MD - 12.13 MPa (1759.95 psi) |
|
Elongation at Break |
ASTM D882 Standard Test Method for Tensile Properties of Thin Plastic Sheeting |
MD - 1099.95% |
|
Tear Resistance |
ASTM D1922 Standard Test Method for Propagation Tear Resistance of Plastic Film and Thin Sheeting by Pendulum Method. Gram Force or Millinewton. |
MD – 9.51 N (969.6 gf) |
|
Wetting Tension |
ASTM D2578 Standard Test Method for Wetting Tension of Polyethylene and Polypropylene Films |
Outside - 48 dynes/cm Inside - 48 dynes/cm
|
| Breaking Strength | ASTM D3759 Standard Test Method for Breaking Strength and Elongation of Pressure-Sensitive Tape |
AAMA 711 PASS ≥ 5.71 lbf/in. 1.92 N/mm (11 lbf/in.) |
| Elongation at Break | ASTM D3759 Standard Test Method for Breaking Strength and Elongation of Pressure-Sensitive Tape |
431% |
| Thermal Cycling 90° Peel Adhesion 24 hours | AAMA 711 Section 5.5 Elevated Temperature Exposure | Accelerated Aging with UV Exposure: No objectionable appearance Elevated Temperature Exposure, Level 3 176°F: No objectionable appearance Thermal Cycling: No objectionable appearance Water Immersion: No objectionable appearance |
| 90° Peel Adhesion | AAMA 711 Annex A | PASS: Elevated Temperature Exposure, Level 3 176°F: No signs of peeling of the flashings from the substrate or any signs of buckling or rippling of the flashings. |
|
Adhesion Testing |
||
|
Post-Conditioning 90° Peel Adhesion |
ASTM D3330 Standard Test Method for Peel Adhesion of Pressure-Sensitive Tape. Method F |
AAMA 711 PASS ≥ 1.5 lbf/in. |
|
90° Peel Adhesion |
AAMA 711 |
OSB (APA PS-2, Exposure 1, Smooth Side Out): 368 N/m (2.1 lbf/in) |
|
90° Peel Adhesion |
AAMA 711 |
PASS ≥ 0.26 N/mm (1.5 lbs/in) |